Elasticity moduli and structure of the Fe73.5Cu1Ta3Si15.5B7 alloy

Zbigniew Kaczkowski (Corresponding Author), Luciano Lanotte, Manfred Muller, Pekka Ruuskanen

Research output: Contribution to journalArticleScientificpeer-review

2 Citations (Scopus)

Abstract

Magnetic field dependences of the piezomagnetic dynamics Ζd and moduli of elasticity in the Fe73.5Cu1Ta3Si15.5B7 alloy strips in as-quenched state and after annealing for 1 h in vacuum in the temperature range from 400°C to 600°C were studied. The elasticity moduli were changed from 75 to 210 GPa depending on magnetic bias field and annealing temperature. A crystalline structure having nanometer sized crystals was observed after annealing at 500°C.
Original languageEnglish
Pages (from-to)746-750
Number of pages5
JournalJournal of Non-Crystalline Solids
Volume250-252
DOIs
Publication statusPublished - 1999
MoE publication typeA1 Journal article-refereed

Fingerprint

Elasticity
elastic properties
Annealing
annealing
strip
modulus of elasticity
Elastic moduli
Vacuum
Magnetic fields
Crystalline materials
Temperature
vacuum
Crystals
temperature
magnetic fields
crystals

Cite this

Kaczkowski, Zbigniew ; Lanotte, Luciano ; Muller, Manfred ; Ruuskanen, Pekka. / Elasticity moduli and structure of the Fe73.5Cu1Ta3Si15.5B7 alloy. In: Journal of Non-Crystalline Solids. 1999 ; Vol. 250-252. pp. 746-750.
@article{287c00e6248f40caac96791abc0ef3ee,
title = "Elasticity moduli and structure of the Fe73.5Cu1Ta3Si15.5B7 alloy",
abstract = "Magnetic field dependences of the piezomagnetic dynamics Ζd and moduli of elasticity in the Fe73.5Cu1Ta3Si15.5B7 alloy strips in as-quenched state and after annealing for 1 h in vacuum in the temperature range from 400°C to 600°C were studied. The elasticity moduli were changed from 75 to 210 GPa depending on magnetic bias field and annealing temperature. A crystalline structure having nanometer sized crystals was observed after annealing at 500°C.",
author = "Zbigniew Kaczkowski and Luciano Lanotte and Manfred Muller and Pekka Ruuskanen",
year = "1999",
doi = "10.1016/S0022-3093(99)00172-6",
language = "English",
volume = "250-252",
pages = "746--750",
journal = "Journal of Non-Crystalline Solids",
issn = "0022-3093",
publisher = "Elsevier",

}

Elasticity moduli and structure of the Fe73.5Cu1Ta3Si15.5B7 alloy. / Kaczkowski, Zbigniew (Corresponding Author); Lanotte, Luciano; Muller, Manfred; Ruuskanen, Pekka.

In: Journal of Non-Crystalline Solids, Vol. 250-252, 1999, p. 746-750.

Research output: Contribution to journalArticleScientificpeer-review

TY - JOUR

T1 - Elasticity moduli and structure of the Fe73.5Cu1Ta3Si15.5B7 alloy

AU - Kaczkowski, Zbigniew

AU - Lanotte, Luciano

AU - Muller, Manfred

AU - Ruuskanen, Pekka

PY - 1999

Y1 - 1999

N2 - Magnetic field dependences of the piezomagnetic dynamics Ζd and moduli of elasticity in the Fe73.5Cu1Ta3Si15.5B7 alloy strips in as-quenched state and after annealing for 1 h in vacuum in the temperature range from 400°C to 600°C were studied. The elasticity moduli were changed from 75 to 210 GPa depending on magnetic bias field and annealing temperature. A crystalline structure having nanometer sized crystals was observed after annealing at 500°C.

AB - Magnetic field dependences of the piezomagnetic dynamics Ζd and moduli of elasticity in the Fe73.5Cu1Ta3Si15.5B7 alloy strips in as-quenched state and after annealing for 1 h in vacuum in the temperature range from 400°C to 600°C were studied. The elasticity moduli were changed from 75 to 210 GPa depending on magnetic bias field and annealing temperature. A crystalline structure having nanometer sized crystals was observed after annealing at 500°C.

U2 - 10.1016/S0022-3093(99)00172-6

DO - 10.1016/S0022-3093(99)00172-6

M3 - Article

VL - 250-252

SP - 746

EP - 750

JO - Journal of Non-Crystalline Solids

JF - Journal of Non-Crystalline Solids

SN - 0022-3093

ER -