High cycle spectrum fatigue of welded components: Dissertation

Keyphrases

• Beam Component 100%
• Box Beam 100%
• Butt Weld 25%
• Car Industry 25%
• Carbon Steel 75%
• Constant Amplitude Fatigue 25%
• Cut-off Limit 25%
• Cycle Fatigue 25%
• Cycle Spectrum 100%
• Cycles to Failure 25%
• Design Curves 50%
• Failure Criterion 25%
• Fatigue Damage 50%
• Fatigue Data 25%
• Fatigue Limit 50%
• Fatigue Test 25%
• Fillet Weld 75%
• High-cycle 100%
• Life Test 25%
• Line Extension 25%
• Load Spectrum 25%
• Loading Spectrum 25%
• Long Crack 25%
• Railcar 25%
• S-N Curve 25%
• Significant Damage 50%
• Small Cycles 75%
• Specimen Geometry 25%
• Spectral Fatigue 100%
• Spot Measurements 25%
• Stainless Steel 50%
• Steel Fatigue 25%
• Steel Weldments 25%
• Straight Line 25%
• Strain Measurement 25%
• Stress Range 25%
• Weld Design 25%
• Weld Fatigue 25%
• Weld Geometry 25%
• Weld Quality 25%
• Welded Components 100%
• Welded Specimen 50%

Engineering

• Carbon Steel 75%
• Conservative Estimate 75%
• Constant Amplitude Fatigue Limit 25%
• Cycle Fatigue 25%
• Experimental Result 25%
• Failure Criterion 25%
• Fatigue Damage 50%
• Fatigue Limit 25%
• Fillet Weld 75%
• Hot Spot 75%
• Life Test 25%
• Mechanical Fatigue Test 25%
• S-N Curve 25%
• Specimen Geometry 25%
• Spectrum Loading 25%
• Stainless Steel 50%
• Straight Line 25%
• Stress Range 25%
• Weld Quality 25%
• Welds 100%

INIS

• amplitudes 11%
• beams 44%
• butt welds 11%
• carbon steels 33%
• cars 11%
• cracks 11%
• curves 44%
• damage 55%
• data 33%
• design 22%
• failures 33%
• fatigue 100%
• geometry 22%
• hot spots 33%
• industry 11%
• levels 11%
• loading 11%
• peaks 11%
• range 22%
• reviews 11%
• spectra 100%
• stainless steels 22%
• strains 11%
• valleys 11%
• welds 77%