INIS
dynamics
100%
alloys
100%
reactors
100%
steels
100%
fractures
100%
pressure vessels
100%
hydrogen embrittlement
100%
strain aging
100%
high temperature
66%
water
33%
hydrogenation
33%
microstructure
33%
hydrogen
33%
air
33%
cracks
33%
crack growth
33%
cleavage
33%
fracture mechanics
33%
Keyphrases
Fracture Resistance
100%
Low Alloy
100%
Reactor Pressure Vessel Steel
100%
High Dynamic
100%
Hydrogen Embrittlement
100%
Dynamic Strain Aging
100%
Hydrogenated
33%
Crack Growth
33%
High Temperature Water
33%
Fracture Mechanics
33%
Microstructural Characterization
33%
Crack Tip
33%
Aging Susceptibility
33%
Quasi-cleavage
33%
High Air Temperature
33%
Hydrogen-induced Softening
33%
Material Science
Fracture Toughness
100%
Dynamic Strain Aging
100%
Hydrogen Embrittlement
100%
Crack Growth
33%
Fracture Mechanics
33%
Crack Tip
33%