Moduli of elasticity of the Fe72.5Cu1Nb4Si13.5B9 amorphous alloy

Zbigniew Kaczkowski; Pekka Ruuskanen; Antal Lovas

doi:10.1016/S0304-8853(02)00794-1

Moduli of elasticity of the Fe_72.5Cu₁Nb₄Si_13.5B₉ amorphous alloy

Zbigniew Kaczkowski (Corresponding Author), Pekka Ruuskanen, Antal Lovas

VTT Technical Research Centre of Finland

Research output: Contribution to journal › Article › Scientific › peer-review

1 Citation (Scopus)

Abstract

The moduli of elasticity as a function of the bias magnetic field and annealing temperature were investigated in the Fe_72.5Cu₁Nb₄Si_13.5B₉ alloy. The minimum of the modulus EH (=63 GPa) was measured after annealing at 450°C. After annealing at 550°C a nanocrystalline structure was observed and E_H and E_Breached 190 GPa.

Original language	English
Pages (from-to)	164-166
Journal	Journal of Magnetism and Magnetic Materials
Volume	254-255
DOIs	https://doi.org/10.1016/S0304-8853(02)00794-1
Publication status	Published - 2003
MoE publication type	A1 Journal article-refereed
Event	15th International Conference on Soft Magnetic Materials - Bilbao, Spain Duration: 5 Sept 2001 → 7 Sept 2001

Keywords

Heat-treatment
metallic glasses
elasticity moduli
ultrasound velocities

Access to Document

10.1016/S0304-8853(02)00794-1

Cite this

@article{a3a5b35c1e404c0d8372d58e98b07e3f,

title = "Moduli of elasticity of the Fe72.5Cu1Nb4Si13.5B9 amorphous alloy",

abstract = "The moduli of elasticity as a function of the bias magnetic field and annealing temperature were investigated in the Fe72.5Cu1Nb4Si13.5B9 alloy. The minimum of the modulus EH (=63 GPa) was measured after annealing at 450°C. After annealing at 550°C a nanocrystalline structure was observed and EH and EB reached 190 GPa.",

keywords = "Heat-treatment, metallic glasses, elasticity moduli, ultrasound velocities",

author = "Zbigniew Kaczkowski and Pekka Ruuskanen and Antal Lovas",

year = "2003",

doi = "10.1016/S0304-8853(02)00794-1",

language = "English",

volume = "254-255",

pages = "164--166",

journal = "Journal of Magnetism and Magnetic Materials",

issn = "0304-8853",

publisher = "Elsevier",

note = "15th International Conference on Soft Magnetic Materials, SMM15 ; Conference date: 05-09-2001 Through 07-09-2001",

}

TY - JOUR

T1 - Moduli of elasticity of the Fe72.5Cu1Nb4Si13.5B9 amorphous alloy

AU - Kaczkowski, Zbigniew

AU - Ruuskanen, Pekka

AU - Lovas, Antal

PY - 2003

Y1 - 2003

N2 - The moduli of elasticity as a function of the bias magnetic field and annealing temperature were investigated in the Fe72.5Cu1Nb4Si13.5B9 alloy. The minimum of the modulus EH (=63 GPa) was measured after annealing at 450°C. After annealing at 550°C a nanocrystalline structure was observed and EH and EB reached 190 GPa.

AB - The moduli of elasticity as a function of the bias magnetic field and annealing temperature were investigated in the Fe72.5Cu1Nb4Si13.5B9 alloy. The minimum of the modulus EH (=63 GPa) was measured after annealing at 450°C. After annealing at 550°C a nanocrystalline structure was observed and EH and EB reached 190 GPa.

KW - Heat-treatment

KW - metallic glasses

KW - elasticity moduli

KW - ultrasound velocities

U2 - 10.1016/S0304-8853(02)00794-1

DO - 10.1016/S0304-8853(02)00794-1

M3 - Article

SN - 0304-8853

VL - 254-255

SP - 164

EP - 166

JO - Journal of Magnetism and Magnetic Materials

JF - Journal of Magnetism and Magnetic Materials

T2 - 15th International Conference on Soft Magnetic Materials

Y2 - 5 September 2001 through 7 September 2001