TY - JOUR
T1 - Study of Fusion Boundary Microstructure and Local Mismatch of SA508/Alloy 52 Dissimilar Metal Weld with Buttering
AU - Hytönen, Noora
AU - Ge, Yanling
AU - Que, Zaiqing
AU - Lindqvist, Sebastian
AU - Nevasmaa, Pekka
AU - Virkkunen, I.
AU - Efsing, P.
N1 - The authors wish to express their gratitude for the funding and support from Ringhals AB, OKG AB, Teollisuuden Voima Oyj and VTT Technical Research Centre of Finland within the FEMMA (Forum for the Effect of Thermal Ageing and Microstructure on Mechanical and EAC Behavior of Ni-based Alloy Dissimilar Metal Welds) research project. The authors also thank NKS for funding the NKS-FEMMA
(AFT/NKS-R(22)134/4) project.
PY - 2023/9
Y1 - 2023/9
N2 - A SA508/Alloy 52 dissimilar metal weld (DMW) mock-up with double-sided Alloy 52 butterings, which is fully representative of Ringhals pressurizer surge nozzle DMW repair solution, was studied. The microstructure, crystal structure, elemental diffusion, carbide formation and macro-, micro- and nano-hardness of the SA508/nickel-base Alloy 52 buttering fusion boundary (FB) were investigated. Three types of FBs were analyzed, i.e., narrow FB (∼80–85% of whole FB), tempered martensitic transition region (∼15%) and wide partially mixed zone (∼1–2%). The different FB types were induced by the local heat flow and respective elementary diffusion, which significantly influence the local hardness mismatch across the DMW interface and the local brittle fracture behavior.
AB - A SA508/Alloy 52 dissimilar metal weld (DMW) mock-up with double-sided Alloy 52 butterings, which is fully representative of Ringhals pressurizer surge nozzle DMW repair solution, was studied. The microstructure, crystal structure, elemental diffusion, carbide formation and macro-, micro- and nano-hardness of the SA508/nickel-base Alloy 52 buttering fusion boundary (FB) were investigated. Three types of FBs were analyzed, i.e., narrow FB (∼80–85% of whole FB), tempered martensitic transition region (∼15%) and wide partially mixed zone (∼1–2%). The different FB types were induced by the local heat flow and respective elementary diffusion, which significantly influence the local hardness mismatch across the DMW interface and the local brittle fracture behavior.
KW - Alloy 52
KW - Buttering
KW - Characterization
KW - Dissimilar metal weld
KW - Fusion boundary
UR - http://www.scopus.com/inward/record.url?scp=85151561824&partnerID=8YFLogxK
U2 - 10.1016/j.jnucmat.2023.154558
DO - 10.1016/j.jnucmat.2023.154558
M3 - Article
SN - 0022-3115
VL - 583
JO - Journal of Nuclear Materials
JF - Journal of Nuclear Materials
M1 - 154558
ER -